Šíření únavové trhliny ve slitině na bázi Fe3Al při zkouškách za zvýšených teplot

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F04%3A04101888" target="_blank" >RIV/68407700:21340/04:04101888 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fatigue Crack Propagation in an Fe3Al Based Alloy Tested at Elevated Temperatures

Popis výsledku v původním jazyce

The fatigue fracture properties of the hot rolled Fe-28at.%Al intermetallic alloy with the addition of chromium and cerium were studied at elevated temperatures. The fatigue crack growth rate curves were measured at 20, 300 and 500°C. The alloy presentsthe best resistance against the fatigue crack growth at 300°C, except for the low values of delta K. Fractographic analysis carried out on fracture surfaces of ruptured specimens revealed several failure mechanisms of crack propagation. The main fatiguecrack growth mechanism at all studied temperatures is transgranular cleavage. The fatigue fracture surface shows a varied micromorphology. Besides transgranular cleavage, transgranular quasi-cleavage, ductile fatigue and brittle striations were found. Inthe zone of final fracture, the material showed an increasing capacity of plastic deformation with increasing temperature. Fracture mechanism changed from transgranular cleavage at 20°C to ductile dimpled fracture at 500°C.

Název v anglickém jazyce

Fatigue Crack Propagation in an Fe3Al Based Alloy Tested at Elevated Temperatures

Popis výsledku anglicky

The fatigue fracture properties of the hot rolled Fe-28at.%Al intermetallic alloy with the addition of chromium and cerium were studied at elevated temperatures. The fatigue crack growth rate curves were measured at 20, 300 and 500°C. The alloy presentsthe best resistance against the fatigue crack growth at 300°C, except for the low values of delta K. Fractographic analysis carried out on fracture surfaces of ruptured specimens revealed several failure mechanisms of crack propagation. The main fatiguecrack growth mechanism at all studied temperatures is transgranular cleavage. The fatigue fracture surface shows a varied micromorphology. Besides transgranular cleavage, transgranular quasi-cleavage, ductile fatigue and brittle striations were found. Inthe zone of final fracture, the material showed an increasing capacity of plastic deformation with increasing temperature. Fracture mechanism changed from transgranular cleavage at 20°C to ductile dimpled fracture at 500°C.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F02%2F0687" target="_blank" >GA106/02/0687: Úprava vlastností intermetalik na bázi Fe3Al termomechanickým zpracováním a aditivy</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

42

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

9

Strana od-do

156-164

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—