Polarizované elektroluminiscence z dvojvrstvových struktur
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F70883521%3A28110%2F04%3A63502382" target="_blank" >RIV/70883521:28110/04:63502382 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Polarized electrolumineseence from bilayer structures
Popis výsledku v původním jazyce
The photoalignment ability of poly[methyl(phenyl)silylene] (PMPSi) films makes it possible to use them as hole-transporting substrates for the preparation of organic oriented films. A PMPSi layer prepared by spin coating was irradiated, after drying, with linearly polarized UV light. Then, water-soluble hydroxyaluminium phthalocyaninesulfonate [Al(OH)Pc(SO3Na)(1-2)] was deposited by casting. The cell ITO/PMPSi/AI(OH)Pc(SO3Na)(1-2)/Al showed non-linear current-voltage characteristics. For applied voltages higher than 10 V, polarized electroluminescence was observed. Its spectral characteristic consisted of two peaks with maxima at about 320 and 700 nm; their polarized anisotropies R-EL = Phi(parallel to) / Phi(perpendicular to) were ca. 15 and 0.5, respectively.
Název v anglickém jazyce
Polarized electrolumineseence from bilayer structures
Popis výsledku anglicky
The photoalignment ability of poly[methyl(phenyl)silylene] (PMPSi) films makes it possible to use them as hole-transporting substrates for the preparation of organic oriented films. A PMPSi layer prepared by spin coating was irradiated, after drying, with linearly polarized UV light. Then, water-soluble hydroxyaluminium phthalocyaninesulfonate [Al(OH)Pc(SO3Na)(1-2)] was deposited by casting. The cell ITO/PMPSi/AI(OH)Pc(SO3Na)(1-2)/Al showed non-linear current-voltage characteristics. For applied voltages higher than 10 V, polarized electroluminescence was observed. Its spectral characteristic consisted of two peaks with maxima at about 320 and 700 nm; their polarized anisotropies R-EL = Phi(parallel to) / Phi(perpendicular to) were ca. 15 and 0.5, respectively.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CD - Makromolekulární chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA202%2F01%2F0518" target="_blank" >GA202/01/0518: Metastabilita v organo-křemíkových hybridních strukturách s proměnnou dimenzionalitou</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Macromolecular symposia
ISSN
1022-1360
e-ISSN
—
Svazek periodika
—
Číslo periodika v rámci svazku
212
Stát vydavatele periodika
DE - Spolková republika Německo
Počet stran výsledku
6
Strana od-do
441-446
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—