Analysis of Fatigue Crack Propagation and Crack Shielding in Super Duplex Stainless Steel and its Welds
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F08%3APU75868" target="_blank" >RIV/00216305:26210/08:PU75868 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Analysis of Fatigue Crack Propagation and Crack Shielding in Super Duplex Stainless Steel and its Welds
Popis výsledku v původním jazyce
Fatigue crack propagation behaviour in super duplex austenitic-ferritic stainless steel and its weld was analysed. ÄK-decreasing tests were performed and the fatigue crack growth rate (FCGR) data were generated. Fatigue crack closure was evaluated by processing the mechanical compliance data stored during the experiments. Fatigue crack branching was assessed based on the edge-filtering of high resolution light optical microscopy images. Although the comparison of the crack behaviour in the base materialand the welded material was complicated by an irregular crack path within the welded specimen, distinctive differences of all evaluated characteristics were observed.
Název v anglickém jazyce
Analysis of Fatigue Crack Propagation and Crack Shielding in Super Duplex Stainless Steel and its Welds
Popis výsledku anglicky
Fatigue crack propagation behaviour in super duplex austenitic-ferritic stainless steel and its weld was analysed. ÄK-decreasing tests were performed and the fatigue crack growth rate (FCGR) data were generated. Fatigue crack closure was evaluated by processing the mechanical compliance data stored during the experiments. Fatigue crack branching was assessed based on the edge-filtering of high resolution light optical microscopy images. Although the comparison of the crack behaviour in the base materialand the welded material was complicated by an irregular crack path within the welded specimen, distinctive differences of all evaluated characteristics were observed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Multilevel Approach to Fracture of Materials, Components and Structures (ECF17)
ISBN
9781617823190
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
2401-2406
Název nakladatele
Vutium
Místo vydání
Brno
Místo konání akce
Brno
Datum konání akce
2. 9. 2008
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—