Determination of mechanical properties from microcompression test

Popis výsledku v původním jazyce

This paper describes a microcompression test of Al - 1.5 wt. % Cu thin film deposited on Si substrate. Microcompression combines the sample preparation with the use of ion focused beam (FIB) with a compression test carried out using nanoindenter. Cylindrical specimens (pillars) were prepared using FIB. The diameter of pillars was about 1.3 microns and their height was about 2 microns (equal to the film thickness). Stress-strain curves of the thin film were obtained. The results depend on crystallographic orientation of pillar. The paper is focused to an attempt to determine as precisely as possible Young modulus of the film using experimental data and finite element modelling.

Název v anglickém jazyce

Determination of mechanical properties from microcompression test

Popis výsledku anglicky

This paper describes a microcompression test of Al - 1.5 wt. % Cu thin film deposited on Si substrate. Microcompression combines the sample preparation with the use of ion focused beam (FIB) with a compression test carried out using nanoindenter. Cylindrical specimens (pillars) were prepared using FIB. The diameter of pillars was about 1.3 microns and their height was about 2 microns (equal to the film thickness). Stress-strain curves of the thin film were obtained. The results depend on crystallographic orientation of pillar. The paper is focused to an attempt to determine as precisely as possible Young modulus of the film using experimental data and finite element modelling.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Sborník Engineering Mechanics 2012

ISBN

978-80-86246-40-6

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1435-1440

Název nakladatele

Neuveden

Místo vydání

Neuveden

Místo konání akce

Svratka

Datum konání akce

14. 5. 2012

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—