Stress Corrosion Cracking and Copper Alloy Products

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F22%3AN0000032" target="_blank" >RIV/25797000:_____/22:N0000032 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.journalmt.com/artkey/mft-202201-0012_stress-corrosion-cracking-and-copper-alloy-products.php" target="_blank" >https://www.journalmt.com/artkey/mft-202201-0012_stress-corrosion-cracking-and-copper-alloy-products.php</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Stress Corrosion Cracking and Copper Alloy Products

Popis výsledku v původním jazyce

Stress corrosion cracking (SCC) is a common cause of structural failure. The simultaneous action of the corrosive environment and tensile stresses creates cracks that have an intercrystalline or transcrystalline character. These are cracks with a fragile morphology of the fracture surface without signs of plastic deformation in their vicinity. SCC cracks occur in several alloys. This paper focuses on copper alloys in which this type of failure occurs frequently. Examples from practice show cases where the occurrence of SCC violation was related to the conditions of use of components and their production technologies. The paper does not aim to capture all the influences associated with the occurrence of SCC failure of copper alloy products.

Název v anglickém jazyce

Stress Corrosion Cracking and Copper Alloy Products

Popis výsledku anglicky

Stress corrosion cracking (SCC) is a common cause of structural failure. The simultaneous action of the corrosive environment and tensile stresses creates cracks that have an intercrystalline or transcrystalline character. These are cracks with a fragile morphology of the fracture surface without signs of plastic deformation in their vicinity. SCC cracks occur in several alloys. This paper focuses on copper alloys in which this type of failure occurs frequently. Examples from practice show cases where the occurrence of SCC violation was related to the conditions of use of components and their production technologies. The paper does not aim to capture all the influences associated with the occurrence of SCC failure of copper alloy products.

Druh

J_ost - Ostatní články v recenzovaných periodicích

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2022

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

2022

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

39-44

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—