Degradation of polyimide and polyethyleneterephtalate irradiated with 150 and 200 keV Ar ions, studied by RBS and ERD techniques.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F00%3A49000202" target="_blank" >RIV/61389005:_____/00:49000202 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Degradation of polyimide and polyethyleneterephtalate irradiated with 150 and 200 keV Ar ions, studied by RBS and ERD techniques.

Popis výsledku v původním jazyce

Polyimide (Upilex, PI) and polyethyleneterephtalate (MylarPET) were irradiated with 200 and 150 keV Ar.sup.+ ions respectively to different fluences and the depth profiles ofhydrogen and oxygen atoms in polymer surface layer were determined using standard Rutherford backscattering (RBS) and elastic recoil detection (ERD) techniques. Significant hydrogen and oxygen depletion is observed at the ion fluences above 1 x 10.sup.14 cm.sup.-2. Above 5 x 10.sup.15 cm.sup.-2 a saturated state is achieved when another fluence increase does not result in significant changes of the H and O profile shape. At higher fluences the H and O depth profiles are rather flat with no local minima. This finding indicates only minor role of nuclear stopping in production of volatile degradation products.

Název v anglickém jazyce

Degradation of polyimide and polyethyleneterephtalate irradiated with 150 and 200 keV Ar ions, studied by RBS and ERD techniques.

Popis výsledku anglicky

Polyimide (Upilex, PI) and polyethyleneterephtalate (MylarPET) were irradiated with 200 and 150 keV Ar.sup.+ ions respectively to different fluences and the depth profiles ofhydrogen and oxygen atoms in polymer surface layer were determined using standard Rutherford backscattering (RBS) and elastic recoil detection (ERD) techniques. Significant hydrogen and oxygen depletion is observed at the ion fluences above 1 x 10.sup.14 cm.sup.-2. Above 5 x 10.sup.15 cm.sup.-2 a saturated state is achieved when another fluence increase does not result in significant changes of the H and O profile shape. At higher fluences the H and O depth profiles are rather flat with no local minima. This finding indicates only minor role of nuclear stopping in production of volatile degradation products.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BG - Jaderná, atomová a molekulová fyzika, urychlovače

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2000

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Nuclear Instruments and Methods. B

ISSN

0168-583X

e-ISSN

—

Svazek periodika

161

Číslo periodika v rámci svazku

N/A

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—