Effect of air annealing on mechanical properties and structure of amorphous B4C films
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989592%3A15310%2F11%3A33116604" target="_blank" >RIV/61989592:15310/11:33116604 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/68378271:_____/11:00363873
Výsledek na webu
<a href="http://dx.doi.org/10.1016/j.surfcoat.2011.02.052" target="_blank" >http://dx.doi.org/10.1016/j.surfcoat.2011.02.052</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.surfcoat.2011.02.052" target="_blank" >10.1016/j.surfcoat.2011.02.052</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of air annealing on mechanical properties and structure of amorphous B4C films
Popis výsledku v původním jazyce
Amorphous B4C films were prepared by magnetron sputtering of the hot-pressed B4C target in different regimes. Hardness, intrinsic stress and film structure were investigated in dependence on the annealing temperature in air. Changes in the film structureand composition were investigated by Raman spectroscopy, confocal microscopy, and electron probe microanalysis.It has been shown that an annealing at 500 °C for 1 h leads to stress reduction, slight thickness decrease and increase of film hardness. However already at 600 °C the film oxidation proceeds very intensively with formation of the phases of boron oxide and amorphous carbon in the surface layer. The thickness of the film decreases quickly.
Název v anglickém jazyce
Effect of air annealing on mechanical properties and structure of amorphous B4C films
Popis výsledku anglicky
Amorphous B4C films were prepared by magnetron sputtering of the hot-pressed B4C target in different regimes. Hardness, intrinsic stress and film structure were investigated in dependence on the annealing temperature in air. Changes in the film structureand composition were investigated by Raman spectroscopy, confocal microscopy, and electron probe microanalysis.It has been shown that an annealing at 500 °C for 1 h leads to stress reduction, slight thickness decrease and increase of film hardness. However already at 600 °C the film oxidation proceeds very intensively with formation of the phases of boron oxide and amorphous carbon in the surface layer. The thickness of the film decreases quickly.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
BH - Optika, masery a lasery
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Surface & Coatings Technology
ISSN
0257-8972
e-ISSN
—
Svazek periodika
205
Číslo periodika v rámci svazku
16
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
6
Strana od-do
4052-4057
Kód UT WoS článku
000290187700012
EID výsledku v databázi Scopus
—