Pre-primary stage of low strain rate creep in metals
Popis výsledku v původním jazyce
Primary stage of creep process is a period when the creep rate is decreasing due to microstructure development. The dislocation density evolves to the dynamic equilibrium value related to the stress. In low-strain creep experiments, similar stage of decreasing strain rate is observed along with apparent transition to steady state. Deeper analysis of the parameters of the stage shows that the substance of the process must be different. The main reasons are: i) the strain is too small for dislocation substructure rearrangement, ii) stress and temperature dependencies of the transition strain and relaxation time do not correspond to any of the known primary creep processes, iii) the strain reached during the stage is almost fully recoverable, so that thedeformation is rather anelastic. The transition strain observed in low strain rate experiments thus should be treated as a special ?pre-primary? stage, while the apparent secondary stage is in fact part of the primary creep stage.
Název v anglickém jazyce
Pre-primary stage of low strain rate creep in metals
Popis výsledku anglicky
Primary stage of creep process is a period when the creep rate is decreasing due to microstructure development. The dislocation density evolves to the dynamic equilibrium value related to the stress. In low-strain creep experiments, similar stage of decreasing strain rate is observed along with apparent transition to steady state. Deeper analysis of the parameters of the stage shows that the substance of the process must be different. The main reasons are: i) the strain is too small for dislocation substructure rearrangement, ii) stress and temperature dependencies of the transition strain and relaxation time do not correspond to any of the known primary creep processes, iii) the strain reached during the stage is almost fully recoverable, so that thedeformation is rather anelastic. The transition strain observed in low strain rate experiments thus should be treated as a special ?pre-primary? stage, while the apparent secondary stage is in fact part of the primary creep stage.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/IAA200410701" target="_blank" >IAA200410701: Přechodové jevy při creepu za podmínek vedoucích k velmi malým rychlostem deformace.</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science Forum
ISSN
0255-5476
e-ISSN
—
Svazek periodika
604-605
Číslo periodika v rámci svazku
-
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
6
Strana od-do
—
Kód UT WoS článku
000263555900033
EID výsledku v databázi Scopus
—