Titania seed layers for PZT thin film growth on copper-coated Kapton films
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F09%3A00336552" target="_blank" >RIV/68378271:_____/09:00336552 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Titania seed layers for PZT thin film growth on copper-coated Kapton films
Popis výsledku v původním jazyce
n this work, we investigate the deposition of crystallization-promoting amorphous titania seed layers onto Cu-coated Kapton (R) HN foils for a subsequent PZT thin film fabrication thereon. Ultrathin TiO2-x layers with controlled stoichiometry were deposited by reactive sputtering at low substrate temperatures. X-ray photoelectron spectroscopy revealed that the Ti4+ ion in the seed layer was stable against Ar+ bombardment-induced reduction while CuO was reduced to Cu2O. Adsorbed moisture, organic solvents and carbon contaminations were quickly removed by Ar+ ion bombardment. (111)-textured PZT was fabricated on seed-layer-coated flexible substrates by means of a RF-modulated plasma jet system.
Název v anglickém jazyce
Titania seed layers for PZT thin film growth on copper-coated Kapton films
Popis výsledku anglicky
n this work, we investigate the deposition of crystallization-promoting amorphous titania seed layers onto Cu-coated Kapton (R) HN foils for a subsequent PZT thin film fabrication thereon. Ultrathin TiO2-x layers with controlled stoichiometry were deposited by reactive sputtering at low substrate temperatures. X-ray photoelectron spectroscopy revealed that the Ti4+ ion in the seed layer was stable against Ar+ bombardment-induced reduction while CuO was reduced to Cu2O. Adsorbed moisture, organic solvents and carbon contaminations were quickly removed by Ar+ ion bombardment. (111)-textured PZT was fabricated on seed-layer-coated flexible substrates by means of a RF-modulated plasma jet system.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Integrated Ferroelectrics
ISSN
1058-4587
e-ISSN
—
Svazek periodika
108
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
10
Strana od-do
—
Kód UT WoS článku
000271511000007
EID výsledku v databázi Scopus
—