Wear Resistance of Duplex Coated P/M Vanadis 6 Cold Work Tool Steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F09%3A00159334" target="_blank" >RIV/68407700:21220/09:00159334 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Wear Resistance of Duplex Coated P/M Vanadis 6 Cold Work Tool Steel

Popis výsledku v původním jazyce

The P/M M2 grade high speed steel and the P/M made Vanadis 6 cold tool were plasma nitrided and PVD - coated or plasma nitrided and duplex coated (plasma nitriding + PVD CrN) at various combinations of processing parameters. Surface characteristics likethe microstructure, hardness profiles, nitrogen concentration depth profiles and phase constitution have been investigated. The PVD - coating adhesion onto the strengthened surface via plasma nitriding was examined by the tribological tests with linear contact between the specimen and counterbody, whereas various contact pressure and sliding distance were applied. It has been determined that the temperature of the plasma nitriding has to be at least of 500 oC and the nitrogen rich atmosphere has to be used when a sufficient surface strengthening should be achieved. Effect of subsequent PVD CrN - coating realised on plasma nitrided specimens can be considered as very positive when the specimens were heavily loaded.

Název v anglickém jazyce

Wear Resistance of Duplex Coated P/M Vanadis 6 Cold Work Tool Steel

Popis výsledku anglicky

The P/M M2 grade high speed steel and the P/M made Vanadis 6 cold tool were plasma nitrided and PVD - coated or plasma nitrided and duplex coated (plasma nitriding + PVD CrN) at various combinations of processing parameters. Surface characteristics likethe microstructure, hardness profiles, nitrogen concentration depth profiles and phase constitution have been investigated. The PVD - coating adhesion onto the strengthened surface via plasma nitriding was examined by the tribological tests with linear contact between the specimen and counterbody, whereas various contact pressure and sliding distance were applied. It has been determined that the temperature of the plasma nitriding has to be at least of 500 oC and the nitrogen rich atmosphere has to be used when a sufficient surface strengthening should be achieved. Effect of subsequent PVD CrN - coating realised on plasma nitrided specimens can be considered as very positive when the specimens were heavily loaded.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ME%20837" target="_blank" >ME 837: Úprava povrchů strojních součástí, uzlů a nástrojů s cílem mnohonásobného prodloužení životnosti s použitím modifikace a nanesením nanostrukturních vrstev i povlaků disperzně zpevněných nanočásticemi</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Proceedings International Scientific Conference Material Science and Manufacturing Technology

ISBN

978-80-213-1931-8

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Česká zemědělská univerzita v Praze, Technická fakulta, Katedra materiálu a strojírenské technologie

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

25. 6. 2009

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—