Preparation of High-temperature YBCO Superconductors Thin Films Using Ionized Jet Deposition

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21340%2F24%3A00378626" target="_blank" >RIV/68407700:21340/24:00378626 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Preparation of High-temperature YBCO Superconductors Thin Films Using Ionized Jet Deposition

Popis výsledku v původním jazyce

Construction of future cities will require optimization of mass-production of economically achievable High-temperature superconductors. Ionized Jet Deposition has a potential to overcome the current limitations. We used this method to prepare 11 samples of YBCO superconductor thin films in 2 series scanning the differences in substrate material and substrate temperature. Analysis of film thickness showed strong dependence of growth speed on the deposition pressure. The thickness of the samples ranged between 600 nm and 1400 nm. After annealing and oxidation process qualitative phase analysis showed presence of superconducting phase YBa2Cu3O7-x on all of the samples. Analysis of electrical properties proved superconducting properties of the selected annealed samples with TC ranging from 70 K to 85 K.

Název v anglickém jazyce

Preparation of High-temperature YBCO Superconductors Thin Films Using Ionized Jet Deposition

Popis výsledku anglicky

Construction of future cities will require optimization of mass-production of economically achievable High-temperature superconductors. Ionized Jet Deposition has a potential to overcome the current limitations. We used this method to prepare 11 samples of YBCO superconductor thin films in 2 series scanning the differences in substrate material and substrate temperature. Analysis of film thickness showed strong dependence of growth speed on the deposition pressure. The thickness of the samples ranged between 600 nm and 1400 nm. After annealing and oxidation process qualitative phase analysis showed presence of superconducting phase YBa2Cu3O7-x on all of the samples. Analysis of electrical properties proved superconducting properties of the selected annealed samples with TC ranging from 70 K to 85 K.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2024

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Sborník příspěvků 13. studentské vědecké konference fyziky pevných látek, fotoniky a materiálů

ISBN

978-80-01-07382-7

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

22-27

Název nakladatele

ČVUT, Fakulta jaderná a fyzikálně inženýrská, Katedra inženýrství pevných látek

Místo vydání

Praha

Místo konání akce

Byňov-Nové Hrady

Datum konání akce

3. 9. 2024

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—